Strain Uniformity and Strain Stability of Al-Glass Composites

Abstract

The impact of pressure and the effect of particle size on the mechanical property of Al-Glass composites are reported in this study. The samples area, thickness range and particle size are respectively 34.0 x 35.0 mm2 20.8 - 22.10 mm and 26.5 nm. The constituents of the same particle size were made into solids by applying constant pressure of 300 bars. Results obtained from observation showed that composition of aluminum in glass, compaction pressure and particle size greatly affected the strain-time relationship of the compacted materials. It was revealed that samples were found with strain stability between 10-40 and 80-100 % wt. of Al in composites.